Welding Process of Straight Seam Welded Pipe
Sources: this site Click: Date: 2016-10-7 22:12:35
Longitudinal straight seam welded pipe butt weld joint cross-sectional shape, depending on the thickness of the body to be welded before welding groove and then type two sides. When welding thick steel plate, for penetration in contact at the edges out of various shapes of the groove, so that more easily into the welding rod or wire. Groove patterns are one-sided welding the welding groove and the sides of the groove. When you select groove type, in addition to outside should be considered to ensure penetration welding convenient, less filler metal Chi, small welding deformation and beveling of Longitudinal low cost factor.
Linker connecting the two is in the welding Longitudinal seam formed called weld. Both sides of the weld in the welding welding heat effect will be, but the organization and performance vary, this area is known as the heat affected zone. Welding due to the workpiece material welding materials, Longitudinal welding current so different, after welding may occur in the weld and heat affected zone of overheating, embrittlement, hardening or softening, but also the weldment performance degradation, deterioration of weldability. This need to adjust the welding conditions, before welding weldment interface preheating, post-weld heat when and weld heat treatment can improve the quality of welding weldment quality.
Longitudinal is of two or more homogeneous or heterogeneous material through a combination of diffusion and the question of the atom or molecule is integrally connected to the process, prompting the question of atoms and molecules produce binding and diffusion method is to heat or pressure, or simultaneously heated and pressurized.
In addition, a local weld foot rapid heating and cooling process, the weld zone due to the binding body and four weeks of the workpiece can not freely expand and contract in the weldment after cooling will produce welding stress and deformation. Important product after welding is required to eliminate welding stress, welding distortion correction.
Linker connecting the two is in the welding Longitudinal seam formed called weld. Both sides of the weld in the welding welding heat effect will be, but the organization and performance vary, this area is known as the heat affected zone. Welding due to the workpiece material welding materials, Longitudinal welding current so different, after welding may occur in the weld and heat affected zone of overheating, embrittlement, hardening or softening, but also the weldment performance degradation, deterioration of weldability. This need to adjust the welding conditions, before welding weldment interface preheating, post-weld heat when and weld heat treatment can improve the quality of welding weldment quality.
Longitudinal is of two or more homogeneous or heterogeneous material through a combination of diffusion and the question of the atom or molecule is integrally connected to the process, prompting the question of atoms and molecules produce binding and diffusion method is to heat or pressure, or simultaneously heated and pressurized.
In addition, a local weld foot rapid heating and cooling process, the weld zone due to the binding body and four weeks of the workpiece can not freely expand and contract in the weldment after cooling will produce welding stress and deformation. Important product after welding is required to eliminate welding stress, welding distortion correction.